Stock Sizes of BS970 Rod Manufacturer in India, Have a look on Specification
Check Supplier of EN8A Steel Hexagon Rod Price in Mumbai, also Refer European Standard of BS970 Forged Bar
| Internal Standard | Equivalent Grades | |||||
|---|---|---|---|---|---|---|
| BS | DIN | IS | EN | SAE/AISI | ||
| EN8A | 080A40 | CK45 | 45C8 | EN8A | 1040,1045 | |
Density
7.85 g/cm³
Modulus of Elasticity
210 GPa (30.5 x 10^6 psi)
Thermal Conductivity
45 W/m·K
Thermal Expansion
11.7 x 10^-6 /°C
Melting Point
1425-1540°C (2600-2800°F)
NACE MR0175 EN8A Grade Square Bar stock at Lowest Price in India, and Refer Delivery Conditions of EN8A Standard Rod
- Hot-rolled condition
- Tempering condition
- Solid Solution condition
- Cold drawn (rolled) condition
- Normalizing condition
- Annealing condition
Refer BS970 Black Bar Chemical Composition
Carbon
0.17-0.24
Silicon
0.17-0.37
Mangenese
0.7-1.00
Sulfur
≤0.035
Phosphorus
≤0.035
Chromium
≤0.25
Nickel
≤0.25
Copper
≤0.25
EN8A Steel Hexagon Rod
EN8A Carbon Steel Bright Bar
EN8A Medium Carbon Steel Flat Bar
EN8A BS970 Forged Bar
EN8A Grade Square Bar
EN8A Standard Rod
BS970 EN8A Black Bar
Steel EN8A Cold Drawn Bar
View EN8A Rectangular Bar Material\ Mechanical Properties of Corrosion & Temperature resistant, and Check EN8A vs EN8D Comparison
Tensile Strength (Mpa)
≥380
Yield Strength (Mpa)
≥210
Elongation
≥25
Reduction in Area
≥50
Hardness
≤111HB
| Property | EN8A | EN8D |
|---|---|---|
| Tensile Strength (MPa) | 580 – 660 MPa | 580 – 660 MPa |
| Hardness (BHN) | 179 – 229 BHN | 179 – 229 BHN |
| Yield Strength (MPa) | 305 MPa (Approx.) | 305 MPa (Approx.) |
| Elongation (%) | 16% (Approx.) | 16% (Approx.) |
| Impact Strength (J) | 28 – 30 Joules | 28 – 32 Joules |
| Density | 7.85 g/cm³ | 7.85 g/cm³ |
| Modulus of Elasticity | 200 GPa | 200 GPa |
| Export to | Price changes and the expected delivery |
|---|---|
| Vietnam | 5 % extra | 14 days |
| Sri Lanka | 5 % extra | 5 days |
| Bangladesh | 5 % extra | 14 days |
| Mayanmar | 5 % extra | 25 days |
| Taiwan | 5 % extra | 15 days |