Table of Content
- EN 25 Round Bar Specification
- Equivalent Material of BS970 EN 25 Hex Bar
- Frequently Used EN25 Round Bar Types
- EN 25 Alloy Steel Rounds Temperature Range
- EN25 vs EN26
- Chemical Composition of EN 25 Grade Square Bar
- EN 25 BS970 Round Bar Physical Properties
- Steel EN 25 Cold Drawn Bar Mechanical Properties
Refer DIN 1.7218 Bright Bar Uses & Applications
Manufacturer of EN25 Round Bar in India, Refer American Standard
| Standard | Value |
|---|---|
| Australia | AS 1444 |
| Great Britain BS970 | Part 3: 1991 |
| BS970 | 1955 – EN25 |
| Germany W.Nr | 1.6743 / 32NiCrMo10-4 |
EN 25 Steel Rod
BS970 EN 25 Hex Bar
EN 25 Grade Steel Flat Bar
Steel EN 25 Square Bar
EN 25 Alloy Steel Rounds
EN 25 Medium Alloy Steel Bright Bar
EN 25 BS970 Forged Bar
EN 25 Grade Black Bar
EN 25 Grade Square Bar manufactured to British Standard BS 970, view Temperature range of EN 25 Hex Bar
| Grade | Tenpreature Range |
|---|---|
| EN25 | 1150°C – 1200°C |
| Property | EN25 | EN26 |
|---|---|---|
| Chemical Composition | C: 0.50% Cr: 0.25% Mn: 0.30% |
C: 0.40% Cr: 0.50% Mn: 0.30% |
| Tensile Strength | 850 – 1000 MPa | 700 – 900 MPa |
| Yield Strength | 600 – 800 MPa | 500 – 700 MPa |
| Hardness | 30 – 34 HRC | 28 – 32 HRC |
| Applications |
|
|
| Machinability | Good, with care | Good, but slightly less than EN25 |
| Weldability | Moderate | Moderate |
Stockist of EN 25 BS970 Round Bar, Refer PMI test and Chemical Compositiion
Carbon
.27 – .35
Mangenese
.50 – .70
Silicon
.10 – .35
Sulfur
.040
Phosphorus
.50 – .80
Nickel
2.30 – 2.80
Density
7.85 g/cm³
Modulus of Elasticity
210 GPa (30.5 x 10^6 psi)
Thermal Conductivity
45 W/m·K
Thermal Expansion
11.7 x 10^-6 /°C
Melting Point
1425-1540°C (2600-2800°F)
Check EN 25 Standard Hexagonal Bar Yield & Tensile Strength table
Condition
Annealed
Tensile Strength
80 (551)
Yeild Strength
35 (241)
Elongation
30 %
| Export to | Price changes and the expected delivery |
|---|---|
| Trinidad And Tobago | 5 % extra | 60 days |
| Jamaica | 5 % extra | 50 days |
| Bahamas | 5 % extra | 60 days |
| Denmark | 5 % extra | 35 days |
| Russia | 5 % extra | 20 days |