Table of Content
AISI 1060 Bright Bar Internal defects testing according to OENORM-M3002 class 3, Refer Specification
AISI 1060 Round Bar Diameter
WNR 1.1221 Rod Length
Hot Rolled S35c Hex Bar Size
DIN-Ck60 Square Bar Size
JIS S35C Billet Size
AISI 1060 Forged Bar Condition
ASTM A36 Square Bar Tolerance
ASME SA36 Flat Bar Surface
WNR 1.1221 Rounds Technique
DIN-Ck60 Black Bar Applications
ASTM A36 Bright Bar Features
Quality Tests and MTC of ASME SA36 Hexagon Rod
DIN-Ck60 Bars in various Types such as Hexagon, Flat & Square, Check American Standard
| Germany DIN,WNr |
England BS |
Italy UNI |
Spain UNE |
China GB |
Russia GOST |
International ISO |
|---|---|---|---|---|---|---|
| Ck60 | 070M60 CS60 |
C60 | C55k | 60 | 60 60G |
C60E4 |
ASTM A36 Rectangular Bar in Drawn/ Polished finish as per ISO 286-2
- Smooth turned
- Rough Turned
- Polish
- Hot rolled annealed
- Cold (bright) drawn
- Centreless ground
- Bright
- Slit rolled edge
- Pitting Resistance Test
- PMI Testing
- Flattening Test
- Chemical Analysis – Spectro Analysis
- Flaring Test
- Sulphur Test
- Hardness Test
AISI 1060 Forged Bar
WNR 1.1221 Rod
DIN-Ck60 Hex Bar
ASTM A36 Square Bar
ASME SA36 Flat Bar
View Chemical Composition of ASME SA36 Flat Bar before buying
Carbon
0.17-0.24
Silicon
0.17-0.37
Mangenese
>0.7-1.00
Phosphorus
≤0.035
Sulfur
≤0.035
Nickel
≤0.25
Know More About WNR 1.1221 Cold Rolled Round Bar Temperature Resistant
Density
7.85 g/cm³
Melting Point
~1425-1540 °C
Thermal Conductivity
~45 W/m·K
Thermal Expansion
~11.7 µm/m·K
Electrical Resistivity
~0.0005 Ω·m
Elongation (%)
≥25
Yield Strength
≥210
Tensile strength
≥380
Hardness
≤111HB
Reduction in Area
≥50
| Export to | Price changes and the expected delivery |
|---|---|
| Nepal | 5 % extra | 7 days |
| Vietnam | 5 % extra | 10 days |
| Cambodia | 5 % extra | 9 days |
| Thailand | 5 % extra | 7 days |
| Russia | 5 % extra | 20 days |
2 Likes