- S35C Hot Rolled and Forged Round Bar Specification
- Hot Rolled S35c Rod Equivalent Material
- Temperature Range of AISI 1035 Hex Bar
- DIN 1.0501 Flat Bar Forging
- DIN 1.0501 Cold Rolled Round Bar Weight Chart
- Thermal Properties of Hot Rolled S35c Square Bar
- Most Commonly Used JIS S35C Round Bar Types
- JIS S35C Rounds Chemical Composition
- Physical Properties of AISI 1035 Forged Bar
- DIN 1.0501 Bright Bar Mechanical Properties
Wide stock of Cold Drawn & Hot Rolled DIN C35 Rod in India
Hot Rolled S35C ASTM Standard
JIS S35C Round Bar Length
AISI 1035 Hex Bar Diameter
DIN 1.0501 Flat Bar Certification
JIS S35C Hexagonal Bar Processing
AISI 1035 Rectangular Bar Condition
Hot Rolled S35c Square Bar Application
Quality Tests and MTC of JIS S35C Rounds
AISI 1035 Forged Bar Finish
Hot Rolled S35c Rod Tolerance
DIN 1.0501 Bright Bar Uses
Hot Rolled S35c Black Bar Technique
Hot Rolled S35C Hexagonal Bar Supplier in Mumbai, Check Equivalent
| USA | Japan | Germany | U. K | France | Italy | Sweden | China |
|---|---|---|---|---|---|---|---|
| AISI/SAE | JIS | WNr. DIN | BS | AFNOR | UNI | SS | GB |
| 1035 | S35C | 1.1183 Cf35 | 060A35 | XC38TS | C36 | 1572 | 35Mn |
| Annealing | Normalizing | Hardening | Tempering |
|---|---|---|---|
| 840-890ºC | 860-900ºC | 830-860ºC | 550-680ºC |
| Treatment | Condition | Temperature °C |
|---|---|---|
| Soft annealing | +SA | 650-700 |
| Quench & Tempering | +QT | 840-870 |
| Stress relieve annealing | +SRA | 550-650 |
| Normalizing | +N | 840-870 |
| Hot forging | +U | 800-1150 |
| Induction or Flame hardening | I-F | 870-900 |
| Quench & Tempering | +QT | 820-850 |
Check DIN 1.0501 Cold Rolled Round Bar Weight Chart
| Diameter (mm) | Weight (kg/m) |
|---|---|
| 5 | 0.39 |
| 6 | 0.56 |
| 8 | 0.98 |
| 10 | 1.57 |
| 12 | 2.27 |
| 14 | 3.06 |
| 16 | 3.98 |
| 18 | 4.91 |
| 20 | 6.19 |
| 22 | 7.37 |
| 25 | 9.82 |
| 30 | 14.27 |
| 35 | 19.24 |
| 40 | 24.34 |
| 45 | 29.85 |
| 50 | 35.27 |
| Properties | T (°C) | Treatment |
|---|---|---|
| Specific Heat (J/kg-K) | 477 | 50-100 |
| Thermal Conductivity (W/m-K) | 42.7 | 100 |
Hot Rolled S35c Rod
JIS S35C Square Bar
AISI 1035 Hex Bar
DIN 1.0501 Flat Bar
JIS S35C Rounds
AISI 1035 Forged Bar
Refer Chemical Composition of JIS S35C Flat Bar
Carbon
0.32-0.38
Silicon
0.15-0.35
Mangenese
0.60-0.90
Phosphorus
0.03
Sulfur
0.035
Density
7.85 g/cm³
Melting Point
~1425-1540 °C
Thermal Conductivity
~45 W/m·K
Thermal Expansion
~11.7 µm/m·K
Electrical Resistivity
~0.0005 Ω·m
Distributor of AISI 1035 Cold Drawn Bar, View Impact Resistance and Strength
Elongation (%)
20
Yield Strength
315 σs/M Pa Min
Tensile strength
530 σb/M Pa Min
Hardness
197 HB Max
Contraction Min
45
Impact Min
55
| Export to | Price changes and the expected delivery |
|---|---|
| South Korea | 5 % extra | 7 days |
| Japan | 5 % extra | 7 days |
| Sri Lanka | 5 % extra | 5 days |
| Mayanmar | 5 % extra | 25 days |
| Taiwan | 5 % extra | 15 days |
3 Likes